Peroxide Cured (EPDM) (TXEP111560)

Previous 1 / 7 Next

Peroxide Cured (EPDM) (TXEP111560) EPDM Sheet Rubber Sheet


Features

  • Standard Width : 1000mm
  • Width Range : 100mm - 2000mm
  • Length : 10m
  • Thickness : From 1mm to 50mm
  • Standard Color : Black
  • Work Temperature : -30°C ~ +150°C

Peroxide cured EPDM Rubber sheeting exhibits good weathering resistant, heat resistant, ozone and hot steam resistant. This characteristic is very similar to premium EPDM but with enhanced temperature and better compression set. Peroxide cured EPDM rubber is also safe to drinking water applications, it is suitable for prolonged exposure to drinking water and will not deteriorate when submerged, making it suitable for gasket sealing applications.

Peroxide cured EPDM rubber sheet is the ideal choice for applications related to outdoor weathering, water dam and gasket in water dam and tank.

Advantage

  • Better compression set
  • Higher working temperature up to 150 Celsius
  • Potable water, drinking water applicable
  • Food safe

Applications

  • Automotive
  • Chemical industry
  • Aerospace
  • Fluid power
  • Potable water
  • Power train systems
  • Safety and handling
  • Fuel systems
  • Appliances
  • Food grade
SPECIFICATION TEST METHOD TEST RESULT UNIT
Specific Gravity ASTM D297 1.10 g/cm3
Hardness ASTM D2240 60 +/- 5 Shore A
Tensile Strength ASTM D-412 15 MPa
Elongation ASTM D-412 450 %
Tear Strength ASTM D-624 35 kgf/cm
Compression Set (22 Hours at 70°C) ASTM D-624 20 %
HEAT RESISTANCE AGING (72 HOURS AT 100°C)
Hardness ASTM D2240 +/-15 Shore A
Tensile Strength ASTM D-412 +/-30 %
Elongation ASTM D-412 -50 %

WORKING TEMPERATURE    
In Air -30°C +150°C
In Oil   -
In Water   +150°C

MAIN CHARACTERISTICS

ELASTICITY COMPRESSION ABRASION FLAME FUELS OZONE
Good Excellent Poor Poor Fair Excellent
Please leave your enquiry here, we will reply as soon as possible.
Name*  
Company Name  
Product Interested  
Quantity  
Email*  
Contact No.*  
Attachment  
*only support gif, jpeg, jpg, png, pdf
Messages*  

Switch to Mobile Version