37, Jalan Bakawali 41,
Taman Johor Jaya,
81100 Johor Bahru,
Johor, Malaysia.
+607-2889366
+607-2889266
- Building Material Spacer
- Conveyor Belt
- MPC Belt
- Rubber Belt
- Stamping Foil
- Belt Fastener
- Caterpillar Belt
- Conveyor belt / Open Mesh Belt
- Elevator Belt
- Elevator Bolt
- Elevator Bucket Bolts
- Plastic Elevator Bucket
- PTFE Tape
- Rubber Sheet
- Sealer Belt (PTFE)
- Steel Elevator Bucket
- Others
EAI Marketing Sdn Bhd
37, Jalan Bakawali 41,
Taman Johor Jaya,
81100 Johor Bahru,
Johor, Malaysia.
37, Jalan Bakawali 41,
Taman Johor Jaya,
81100 Johor Bahru,
Johor, Malaysia.
Peroxide Cured (NBR) Rubber Sheet (TXNBR1261360)
| Previous | 1 / 7 | Next |
Features
- Standard Width : 1000mm
- Width Range : 100mm - 2000mm
- Length : 10m
- Thickness : From 1mm to 50mm
- Standard Color : Black
- Work Temperature : -40°C ~ +125°C
Peroxide cured NBR is excellent for long term severe applications where exposure to heat, oil and with exceptional compression set.
ChangRubber peroxide cured NBR rubber sheet with minimum 13mpa is very suitable for extreme applications, it's oil resistant is superb even application with mineral oil class III equivalent. Unlike usually sulfure cured NBR rubber sheet, peroxide cured NBR rubber sheet provides better heat resistance, lower compression sets and better mineral oil resistant.
Peroxide cured NBR rubber sheet serve temperature range from -40 to +125 degree celsuis, this peroxide cured NBR rubber is ideal application in automotive, power plant industry, aircraft industry, drywell heads, pool gates and etc.
Advantage
- Better compression set
- Higher working temperature up to 125 Celsius
- Heat Stability
Applications
- Automotive
- Oil & Gas Industry
- Aerospace
- Fluid power
- Transmission Belts
- Power Train Systems
- Animal Oil
- Fuel Systems
- Dilute Acids
- Food grade
| SPECIFICATION | TEST METHOD | TEST RESULT | UNIT | |
| Specific Gravity | ASTM D297 | 1.26 | g/cm3 | |
| Hardness | ASTM D2240 | 60 +/- 5 | Shore A | |
| Tensile Strength | ASTM D-412 | 13 | MPa | |
| Elongation | ASTM D-412 | 350 | % | |
| Tear Strength | ASTM D-624 | 35 | kgf/cm | |
| Compression Set (22 Hours at 70°C) | ASTM D-395 | <20 | % | |
| HEAT RESISTANCE AGING OIL 903 (72 HOURS AT 100°C) | ||||
| Hardness | ASTM D2240 | -5 | +10 | Shore A |
| Tensile Strength | ASTM D-412 | -40 | % | |
| Elongation | ASTM D-412 | -40 | % | |
| Volume Change | ASTM D-412 | +25 | % | |
| WORKING TEMPERATURE | ||
| In Air | -40°C | +125°C |
| In Oil | +120°C | |
| In Water | +125°C |
MAIN CHARACTERISTICS
| ELASTICITY | COMPRESSION | ABRASION | FLAME | FUELS | OZONE |
| Good | Excellent | Poor | Poor | Excellent | Fair |